1190A 物性表
1190A 是全硫化熱塑性硫化膠(TPV),具有良好的強度、較低的壓縮永久變形、突出的耐候性。
1190A is a cross-linked EPDM/PP compound(TPV). It is featured by excellent strength, compression set and weatherability.
物理性能 Physical property |
典型數值 Typical value |
測試依據 Test method |
肖氏硬度,邵氏A,5秒 Hardness, ShA,5 seconds delayed |
90 | ASTM D2240 |
密度 Density |
0.97g/cm3 | ASTM D792 |
比重 Specific gravity |
0.97 | ASTM D792 |
拉伸強度 Tensile strength |
15MPa | ASTM D412 |
拉伸應力(在100%時) Tensile Modulus @100% |
4.6MPa | ASTM D412 |
斷裂伸長率 Elongation at break |
650% | ASTM D412 |
撕裂強度,C 型 Tear strength, Die C |
50 KN/m | ASTM D624 |
IRM903號油,體積膨脹率(1250C,70小時) IRM903 oil, Vol swell(2820F/1250C,70hr) |
/ | ASTM D471 |
壓縮永久變形(700C,22hr) Compression set (700C,22hr) |
59 % | ASTM D395 |
耐臭氧性(臭氧濃度:500hrs/100pphm) Ozone resistance (500hrs/100pphm ozone conc.) |
A級 Good |
ASTMD1149 |
收縮率 Shrinkage |
1.2-1.6 % | ASTM D955 |
1190A 工藝建議
注塑 Injection |
典型數值 Typical value |
乾燥溫度Drying temp. | 70-800C |
乾燥時間Drying time | 3-4 hr |
後段溫度Rear temp. | 170~180°C |
中段溫度Middle temp. | 180~200°C |
前段溫度Front temp. | 180~200°C |
出口溫度Nozzle temp. | 190~200°C |
加工(熔體)溫度Melt temp. | 190~200°C |
模具溫度Mold temp. | 10~50°C |
背壓Back pressure | 0.3-0.7Mpa |
螺杆轉速Screw speed | 100 ~200 rpm |
更多產品信息,請訪問寧波瀚科網站www.ningbonexlink.com或者諮詢寧波瀚科銷售經理。