10B-60 是全硫化熱塑性硫化膠（TPV），具有良好的強度、較低的壓縮永久變形、突出的耐候性。
10B-60 is a cross-linked EPDM/PP compound（TPV）. It is featured by excellent strength, compression set and weatherability.
|
物理性能 Physical property |
典型數值 Typical value |
測試依據 Test method |
|
肖氏硬度，邵氏A，5秒 Hardness, ShA，5 seconds delayed |
62 | ASTM D2240 |
|
密度 Density |
0.97g/cm3 | ASTM D792 |
|
比重 Specific gravity |
0.97 | ASTM D792 |
|
拉伸強度 Tensile strength |
5.4MPa | ASTM D412 |
|
拉伸應力（在100%時） Tensile Modulus @100% |
2.2MPa | ASTM D412 |
|
斷裂伸長率 Elongation at break |
500% | ASTM D412 |
|
撕裂強度，C 型 Tear strength, Die C |
22.0 KN/m | ASTM D624 |
| IRM903號油，體積膨脹率（1250C，70小時） IRM903 oil, Vol swell(2820F/1250C,70hr) | 93% | ASTM D471 |
| 壓縮永久變形(700C,22hr) Compression set (700C,22hr) | 30% | ASTM D395 |
| 壓縮永久變形(1250C,70hr) Compression set (1250C,70hr) | 42% | ASTM D395 |
|
耐臭氧性（臭氧濃度：500hrs/100pphm） Ozone resistance (500hrs/100pphm ozone conc.) |
A級 Good | ASTMD1149 |
10B-60工藝建議Processing Recommendation
|
擠出 Extrusion |
典型數值 Typical value |
| 乾燥溫度 Drying temp. | 70-800C |
| 乾燥時間 Drying time | 3-4 hr |
| 後段溫度 Rear temp. | 170~180°C |
| 中段溫度 Middle temp. | 180~200°C |
| 前段溫度 Front temp. | 180~200°C |
| 前段溫度 Front temp. | 180~200°C |
| 出口溫度 Die temp. | 190~200°C |
| 加工（熔體）溫度 Melt temp. | 190~200°C |