TPE-1250A 物性表
1250A是熱塑性彈性體（TPE），具有良好的強度、較低的壓縮永久變形、突出的耐候性。
1250A is a Thermoplastic elastomer（TPE）. It is featured by excellent strength, compression set and weatherability.
|
物理特性 Physical Property |
典型數值Typical Value |
測試依據 Test Method |
|
肖氏硬度，邵氏A，5秒 Hardness, ShA，5 seconds delayed |
50 | ASTM D2240 |
|
密度Density |
1.05g/cm3 | ASTM D792 |
|
比重Specific gravity |
1.05 | ASTM D792 |
| 拉伸強度Tensile strength | 3.5MPa | ASTM D412 |
|
拉伸應力（在100%時）Tensile Modulus @100% |
0.8MPa | ASTM D412 |
|
斷裂伸長率Elongation at break |
400% | ASTM D412 |
|
撕裂強度，C 型Tear strength, Die C |
18.0 KN/m | ASTM D624 |
|
IRM903號油，體積膨脹率（1250C，70小時）IRM903 oil, Vol swell(2820F/1250C,70hr) |
/ | ASTM D471 |
|
壓縮永久變形(700C,22hr) Compression set (700C,22hr) |
35 % | ASTM D395 |
|
耐臭氧性（臭氧濃度：500hrs/100pphm） Ozone resistance (500hrs/100pphm ozone conc.) |
A級 Good |
ASTMD1149 |
|
收縮率 Shrinkage |
1.2-1.8 % | ASTM D955 |
TPE-1250A工藝建議 Processing Recommendation
|
注塑Injection molding |
典型數值Typical value |
| 乾燥溫度Drying temp. | 70-800C |
| 乾燥時間Drying time | 3-4 hr |
| 後段溫度Rear temp. | 170~180°C |
| 中段溫度Middle temp. | 180~200°C |
| 前段溫度Front temp. | 180~200°C |
| 出口溫度Nozzle temp. | 190~200°C |
| 加工（熔體）溫度Melt temp. | 190~200°C |
| 模具溫度Mold temp. | 10~50°C |
| 背壓Back pressure | 0.3-0.7Mpa |
| 螺杆轉速Screw speed | 100 ~200 rpm |